Sodium silicate, also known as liquid glass, is a versatile compound used in a variety of industries due to its strong binding, sealing, and protective properties. In water treatment, it helps soften hard water and prevents scale buildup in pipes and boilers. In construction, it is used as a binder in concrete and cement, enhancing strength and water resistance, while also serving as a key ingredient in adhesives for paper, wood, and cardboard products.
1344-09-8
Local
India
| CHARACTERISTICS | ALKALINE GRADE | NEUTRAL GRADE | |||
|---|---|---|---|---|---|
| Type | 52 Baume | 56 Baume | 30 Baume | 30 Baume | 40 Baume |
| Na2o | 14.52% +/- 0.5% | 15.80% +/- 0.5% | 6.30% +/- 0.5% | 6.76% +/- 0.5% | 8.60% +/- 0.5% |
| Sio2 | 32.00% +/- 0.5% | 34.80% +/- 0.5% | 20.80% +/- 1,0% | 22.35% +/- 1.0% | 28.40% +/- 1.0% |
| Total Solid | 46.52% +/- 1.0% | 50.60% +/- 1.0% | 27.10% +/- 1.0% | 29.11% +/- 1.0% | 37.0% +/- 1.0% |
| Ratio | 1:2.20 (Wt Ratio) +/- 0.1 | 1:2.20 (Wit Ratio) +/- 0.1 | 1:3,30 (Wt Ratio) +/- 0.1 | 1:3.30 (Wt Ratio) +/- 0.05 | 1:3.30 (Wt Ratio) +/- 0.1 |
| Baume ( Degree ) | 52 +/- 1.0 | 56 4/-1.0 | 30+/- 0.5 | 32 +/-1.0% | 40 +/-1.0 |
| Sp. Gravity | 1.560 +/- 0.02 | 1,630 +/- 0.02 | 1.260 +/- 0.02 | 1.285 +/- 0.02 | 1.380 +/- 0.02 |
| CHEMICAL COMPOUND | ALKALINE GRADE | NEUTRAL GRADE |
|---|---|---|
| Appearance | Transpherence low melting glass | Transpherence low melting glass |
| PH (5 % Aqus Soin ) | 11 to 12 PH | 11 to12 Pm |
| Na2O Content | 31.22% +/-0,25% | 23.24% +/- 0.50% |
| Sio2 Content | 68.77% +/- 0.25% | 76.75% +/- 0.50% |
| Total Solid | 99.99% +/- 0.1 | 99.99% +/- 0.1% |
| Ratio | 1:2.20 (Wt Ratio) +/- 0,1 % | 1:3.30 (Wt Ratio) +/- 0.1% |
| Iron Content | 250% +/- 100ppm | 200 ppm max |
| Unmelted Sand | 1 % +/- 0.2 % | 1 % +/+0.2% |